1. Description of glass fiber reinforced plastic wall structure
From the inside to the outside, the wall structure of FRP is: FRP lining, FRP secondary lining, FRP winding, FRP external protective layer.
The FRP inner lining layer and the FRP secondary inner lining layer play the role of anti-corrosion and anti-seepage, the winding layer is responsible for the strength and rigidity of the pipeline, and the outer protective layer plays the role of anti-aging, anti-corrosion, and anti-sun.
2.Detailed description of glass fiber reinforced plastic pipeline process
(1) Preparation process
a. Equipment debugging. First, carefully check whether the equipment operation and working parts are normal. In particular, check whether the resin-curing agent two-component pump is clogged and whether the ratio meets the design requirements; ensure the lining, winding, trimming, demoulding and other equipment Stable operation and working accuracy;
b. Clean the mold. The mold surface is required to be free of pits, dust, debris and other attachments, and the mold must be made smooth, and if there is a problem, repair and maintain it in time;
c. Wrap polyester film. In order to facilitate the demolding of the pipe, the surface of the mold should be covered with a layer of polyester film, the overlap width of the film is 1~2cm, and the thickness is between 40um. It is required that the film has no damage, no wrinkles, and both sides are smooth and clean. The quality of the film products meets the requirements of GB 13950-1992.
(2) Lining process
a. Prepared with resin lining. According to the resin formula system made by the quality inspection department according to the working environment and temperature conditions at the time, the lining resin should be blended, and the amount of ingredients should be reasonably controlled according to the manufacturing schedule. When the on-site situation changes, the quality inspection department and the manufacturing department should adjust the formula in time, and prepare the required resin according to the new formula;
b. Preparation of reinforcement materials. According to the design requirements, transport the reinforcement materials needed to make the inner lining to the designated location, and cut and process some wide-format reinforcement materials to the design width;
c. Production of inner lining layer. The inner lining is made according to the design requirements. Reasonable tension should be applied to each single layer during the laying process, and an appropriate amount of overlap should be applied to each other, and the combined pressure roller should be used to repeatedly roll out the air bubbles to ensure that the fiber is completely saturated. And require that each reinforced material layer meet the designed resin content requirements;
d. Preliminary self-inspection. After laying each layer according to the design requirements, the operator is required to perform preliminary quality inspection: whether the inner lining reaches the design thickness, whether there is poor glue or glue hanging in some parts, whether there are white spots, air bubbles, etc., if the above situation occurs Report and take measures in a timely manner;
e. Enter the far-infrared deep curing process of the inner lining.
(3) Far infrared deep curing
FRP pipes must be deep-infrared curing treatment, the purpose is: to improve the curing degree of the inner lining layer, improve the corrosion and temperature resistance of the pipeline;
(4) Process quality inspection
Before winding, reconfirm that the lining has no bubbles, pores, impurities, smooth surface, reasonable resin content, no white spots and poor local curing. It is necessary to carefully check whether the inner lining is qualified, and it is strictly forbidden to wind on the machine if it is unqualified.
(5) Winding process
Input the designed parameters into the microcomputer, and after the lining is solidified, the microcomputer controls the reciprocating winding with alkali-free non-twisted glass fiber to the thickness of the winding layer. Apply an outer protective layer with 100% resin content to the specified thickness. The resin content of the winding layer is generally about 35%, and its thickness depends on the combination of the strength and rigidity of the pipeline design.
(6) Infrared curing
The pipeline enters the curing stage. During the curing process, the mold should be kept rolling at an appropriate speed to make it evenly cured. During the curing process, attention should be paid to monitoring the temperature of the pipe body, and the curing plan should be adjusted reasonably.
(7) Trimming and demoulding:
When the Barcol hardness of the pipe is greater than 30, trim the pipe port. Then use a hydraulic stripper to separate the pipe and the mold, and mark the middle part of the pipe as required.
(8) Pipeline hydraulic test and placement:
Each batch of pipelines is subjected to a hydraulic test according to regulations, filled with water, and the pressure is evenly increased to 1.5 times the design pressure of the pipeline, and maintained for no less than 2 minutes. Carefully check the surface of the pipeline and the pressure gauge. After the pressure test is qualified, the pipeline is supported at two points.
Hebei Yuniu Fiberglass Manufacturing Company Limited is a fiberglass material manufacturer with over 10-year experience, 7- year exporting experience.
We are manufacturer of fiberglass raw materials, Such as fiberglass roving, fiberglass yarn, fiberglass chopped strand mat, fiberglass chopped strands, fiberglass black mat, fiberglass woven roving, fiberglass fabric, fiberglass cloth..And so on.
If any needs, please contact us freely.
We will do our best to help and support you.